> PVDC latex properties |
|
Properties of PVDC latex
|
Barrier properties
Coating on
single-component film:
|
|
Oxygen barrier and
moisture barrier performance is greatly enhanced
by coating with PVDC latex. |
Type of film |
Thickness
(µm) |
Oxygen permeability *2)
(mL/m2/0.1 MPa/day) |
Water vapor
permeability *3)
(g/m2/day) |
K-OPP *1) |
23 |
4 |
4 |
OPP |
20 |
1300 |
7-8 |
Nylon |
15 |
80 |
300 |
PET |
12 |
80 |
45 |
LDPE |
40 |
2000 |
9-12 |
HDPE |
40 |
1500 |
3-6 |
CPP |
40 |
2000 |
6-12 |
|
|
*1) 20 µ OPP film with 3 µ coating of Asahi Kasei PVDC latex L803C
*2) Results with JIS K7126B at 20°C, ≈70%RH
*3) Results with JIS K7129 at 40°C, 90%RH
Note : All values are typical laboratory averages obtained using the specified test methods, and not guaranteed. |
|
Coating with
multi-component film: |
|
Oxygen barrier and moisture
barrier performance is greatly enhanced by including a PVDC latex coating. |
|
Gas barrier performance of multi-component films
Film sample |
Oxygen permeability *1)
(ml/m2/0.1 MPa/day) |
Water vapor permeability *2)
(g/m2/day) |
K-OPP/PE |
10.0 |
3.1 |
OPP/CPP |
>100 |
5.7 |
Ny/PE |
>100 |
9.4 |
|
|
*1) Results with JIS K7126B at 20°C, ≈70%RH
*2) Results with JIS K7129 at 40°C, 90%RH
Note : All values are typical laboratory averages obtained using the specified test methods, and not guaranteed. |
|
Number of days until 2% weight change of packaged food product
Ham
Film sample |
Days |
K-OPP/PE |
20 |
OPP/CPP |
14 |
Ny/PE |
9 |
|
|
|
Peanuts
Film sample |
Days |
K-OPP/PE |
8 |
OPP/CPP |
4 |
Ny/PE |
3 |
|
|
|
|
Yuepin (Chinese confection - Yuebing)
Film sample |
Days |
K-OPP/PE |
35 |
OPP/CPP |
22 |
Ny/PE |
15 |
|
|
Soft cake
Film sample |
Days |
K-OPP/PE |
22 |
OPP/CPP |
10 |
Ny/PE |
10 |
|
|
|
Results with JIS K7129 at 40°C, 90%RH
Film samples
K-OPP/PE: 20 µm PVDC-coated OPP/15 µm PE/25
µm LLDPE
OPP/CPP: 20 µm OPP/dry lamination adhesive/20
µm CPP
Ny/PE: 15 µm nylon/dry lamination adhesive/50
µm LLDPE
Note : All values are typical laboratory averages obtained using the specified test methods, and not guaranteed. |
|